We use cookies to ensure that we give you the best experience on our website. If you click 'Accept all cookies' we'll assume that you are happy to receive all cookies and you won't see this message again. If you click 'Reject all non-essential cookies' only necessary cookies providing core functionality such as security, network management, and accessibility will be enabled. Click 'Find out more' for information on how to change your cookie settings.

Corrosion current pulses associated with the nucleation of microcracks and their movement across single grain boundary facets were detected for intergranular stress corrosion cracking (IGSCC) of sensitised type 304 stainless steel induced by dilute thiosulphate solutions at ambient temperature. Estimates of crack-tip dissolution width and current density were derived. Cracks initiated as a consequence of non-uniform deformation around grain boundaries, and most stopped after penetration of at most a few grain-boundary facets. The idea of microstructural barriers to the propagation of short stress corrosion cracks was developed; such barriers became less important as the chemistry of the environment became more aggressive; a simple statistical model, based on a jump probability to cross a barrier, was developed for crack advance, and in part for the statistics of failure by IGSCC. At higher strain, fatal cracks initiated from a pre-existing microcrack. Strain-induced martensite formation resulted in a decrease with increasing strain in both microcrack nucleation frequency and penetration. © 1991.

Original publication

DOI

10.1016/0010-938X(92)90017-W

Type

Journal article

Journal

Corrosion Science

Publication Date

01/01/1992

Volume

33